Artificial shoe leather Pattern «Frisko»

With combined weave:

Thickness: matched to customer’s wishes

Coating type: PVC100 [%] [%]

Backing type: PES 100 [%]

Flammability: A standard product

Standard width: 145 [cm]

For the production of vinyl artificial shoe leather, polyester thermostable fabrics are used:

Indicator name	Reference on knitwear of combined weave
Breaking load, daN, not less than - longitudinal direction - transverse direction	40 20
Stiffness, cN, not less than - for group 10 - 13 - for group 14 - 17 - for group 20 - 25 - for group 21 (high frost resistance)	3 10 35 60
The bonding strength of the front coating and the backing, daN/5 cm, not less than - longitudinal direction	2,5
Multiple flexing, kilocycles, not less than	100
Light resistance, points, for light tones, not less than	3
Tear resistance, N, not less - longitudinal direction - transverse direction	15 15
Frost resistance,°C, not higher than - products for winter shoes in the usual version - products for winter shoes, frost-resistant - products for summer shoes	minus 25 minus 30 minus 10
Water permeability, hrs, not less than	8

Frost resistance of vinyl artificial leather for summer shoes is determined during the product development and launching into manufacture.

Vinyl artificial shoe leather with a knitted backing is manufactured with nominal width of 140 and 145 cm with tolerances in width ±2 cm. Vinyl artificial leather of other width can be manufactured by agreement or at the request of consumer.

This type of vinyl artificial shoe leather is wound in rolls of a length not more than:

• group 10-11 – 50 linear meters;
• group 12-14 – 40 linear meters;
• group 15-17 – 30 linear meters;
• group 20-25 – 25 linear meters.

fabrics with stockinette structure:

Thickness: matched to customer’s wishes

Coating type: PVC100 [%] [%]

Backing type: PES 100 [%]

Flammability: A standard product

Standard width: 145 [cm]

For the production of vinyls used in captive polyester thermally stabilized:

Indicator name	Reference on knitwear weaving of stockinette structure
Breaking load, daN, not less than - longitudinal direction - transverse direction	20 10
Stiffness, cN, not less than - for group 10 - 13 - for group 14 - 17 - for group 20 - 25 - for group 21 (high frost resistance)	3 10 35 60
The bonding strength of the front coating and the backing, daN/5 cm, not less than - longitudinal direction	2,5
Multiple flexing, kilocycles, not less than	100
Light resistance, points, for light tones, not less than	3
Tear resistance, N, not less - longitudinal direction - transverse direction	12 10
Frost resistance,°C, not higher than - products for winter shoes in the usual version - products for winter shoes, frost-resistant - products for summer shoes	minus 25 minus 30 minus 10
Water permeability, hrs, not less than	8

With non-woven backing:

Thickness: selected individually according to customer criteria

In spite of this, the B-НT type shoe vinyl artificial leather is available in the following thickness groups:

Coating type: PVC100 [%]

Backing type: PES 100 [%]

Flammability: A standard product

Standard width: 145 [cm]

Physical-mechanical indicators of finished products must meet the standards of the Technical Specifications and Technical Characteristics:

Indicator name	Reference
Breaking load, daN, not less than 13 group - longitudinal direction - transverse direction 15 group - longitudinal direction - transverse direction 29 - 31 group - longitudinal direction - transverse direction	14 12 20 17 60 60
Stiffness, cN products for the insole, not less than - 13 – 15 group - 29 group - 31 group products for the insole, not less than	20 40 60 9
Tear resistance, N, not less than - longitudinal direction - transverse direction	12 12

Physical-mechanical indicators of finished products must meet the standards of the Technical Specifications and Technical Characteristics:

• 13 group– 40 m.p.
• 15 group– 30 m.p.
• 29 group– 10 m.p.
• 31 group– 10 m.p.

On a woven basis:

Imported polyester fabric is used for the production of vinyl artificial shoe leather. It is allowed to use other fabrics that provide the necessary physical-mechanical parameters of the finished products in accordance with the Technical Specifications, Technical Characteristics and that meet the requirements of a customer.

Vinyl artificial shoe leather with a woven backing is subject to mandatory stamping on the calender machine. Embossing pattern is as per order.

Thickness: selected individually according to customer criteria.

Vinyl artificial shoe leather with a woven backing is manufactured in the width of 84 – 90 cm. Vinyl artificial leather of other width, incl. 140 cm, can be manufactured by agreement or at the request of a consumer.

Type of coating: PVC 100 [%]

Vinyl artificial shoe leather made with a woven backing must comply with the following physical-mechanical parameters:

Indicator name	Reference
	19 group	20 group	22 group
Weight, g/m2, not less than	900	1000	1100
Breaking load, daN, not less than - longitudinal direction - transverse direction	70 40	70 40	80 50
Extensibility at break, %, not less than - longitudinal direction - transverse direction	13 18
Stiffness, cN, not less than	20	25	30
Frost resistance,°C, not higher than	minus25
Water permeability,, cm3/cm2 x hrs, not less than	1,0
Vapor permeability, mg/cm2x hrs, not less than	1,2
Shrinkage after 2 hrs of wetting, %, not more than - longitudinal direction - transverse direction	5 0,5
Wear, g/kW x hrs, not more than	425

This type of vinyl artificial shoe leather is wound in rolls of a length not more than:

• group 19 – 25 linear meters;
• group 20–22 – 20 linear meters.

Skin color can be selected according to the RAL table. The shades may differ due to the unique color rendering of your screen