Non-woven backing:
Thickness: selected individually according to customer criteria
Coating type: PVC100 [%]
Backing type: PES 100 [%]
Flammability: A standard product
Standard width: 145 [cm]
Standard roll sleeve: 40 [m]
Indicator name | Reference |
---|---|
Breaking load, daN, not less than - longitudinal direction - transverse direction |
15 10 |
Extensibility at break, % - longitudinal direction - transverse direction |
10-60 50-160 |
Resistance of front coating to dry and wet friction, points, not less than | 4 |
Stiffness, cN, not more than | 20 |
Multiple flexing, kilocycles, not less than | 50 |
Light resistance, points, for light tones, not less than | 4 |
For dressed fabrics
Leather on this backing is characterized by high strength, low stiffness.
Thickness: matched to customer’s wishes, the following groups of thicknesses can be produced:
group of thicknesses | 15 | 16 | 17 |
thickness, mm | 1,0 ± 0,1 | 1,1 ± 0,1 | 1,2 ± 0,1 |
weight 1m2/g, not less than | 400 | 450 | 550 |
Coating type: PVC100 [%]
Backing type: PES 100 [%]
Flammability: A standard product
Standard width: 145 [cm]
Standard roll sleeve: 40 [m]
Indicator name | Reference |
---|---|
Breaking load, daN, not less than - longitudinal direction - transverse direction |
40 30 |
Extensibility at break, %, % - - longitudinal direction - transverse direction |
40 – 90 60 – 130 |
The bonding strength of the front coating and the backing, daN/5 cm, not less than - longitudinal direction - transverse direction |
25 25 |
Resistance to dry and wet friction, points, not less than | 4 |
Stiffness, cN, not more than | 20 |
Multiple flexing, kilocycles, not less than | 100 |
Light resistance, points, for light tones, not less than | 4 |
Time of permeability of petroleum products, oils, water, hrs, not less than | 24 |
For double-layered knitted fabric (weave “Radier”)
It is characterized by a much larger transverse elongation compared to knitted fabrics of other weaves. Accordingly, it is more technologically convenient to work where the leather should be stretched to the structure.
Thickness: matched to customer’s wishes
Coating type: PVC100 [%]
Backing type: PES 100 [%]
Flammability: A standard product
Standard width: 145 [cm]
Standard roll sleeve: 40 [m]
Indicator name | Reference |
---|---|
Breaking load, daN, not less than - longitudinal direction |
40 |
Extensibility at break, % - longitudinal direction - transverse direction |
35 – 50 >180 |
The bonding strength of the front coating and the backing, daN/5 cm, not less than - longitudinal direction - transverse direction |
5,0 4,0 |
Resistance to dry and wet friction, points, not less than | 4 |
Stiffness, cN, not more than | 30 |
Multiple flexing, kilocycles, not less than | 130 |
Light resistance, points, for light tones, not less than | 4 |
Time of permeability of petroleum products, oils, water, hrs, not less than | 10 |
Vinyl leather on knitted fabrics with combined weave (chevron, crepe)
Includes knitted fabrics with overlapping weaves – this allows to obtain the durability and stretching required by a customer.
Thickness: matched to customer’s wishes
Coating type: PVC100 [%]
Backing type: PES 100 [%]
Flammability: A standard product
Standard width: 145 [cm]
Standard roll sleeve: 40 [m]
The items are selected individually according to customer's requirements regarding the physical-mechanical properties of vinyl leather (1-3):
Indicator name | Reference | ||
---|---|---|---|
1 | 2 | 3 | |
Breaking load, daN, not less than - longitudinal direction - transverse direction |
40 20 |
50 20 |
40 30 |
Extensibility at break, % - longitudinal direction - transverse direction |
40 20 |
50 20 |
40 30 |
The bonding strength of the front coating and the backing, daN/5 cm, not less than - longitudinal direction |
3,0 |
||
Resistance to dry and wet friction, points, not less than | 4 | ||
Stiffness, cN, not more than | 30 | ||
Multiple flexing, kilocycles, not less than | 40 | ||
Light resistance, points, for light tones, not less than | 4 | ||
Time of permeability of petroleum products, oils, water, hrs, not less than | 24 |
Vinyl leather on knitted fabrics with ‘stockinette structure’ weave
The production of this weave is characterized by less elongation in the transverse direction, better durability.
The items are selected individually according to customer’s requirements regarding the physical and mechanical properties of vinyl leather (in the spaces 1-4):
Indicator name | Reference | |||
---|---|---|---|---|
1 | 2 | 3 | 4 | |
Breaking load, daN, not less than - longitudinal direction - transverse direction |
25 - |
20 15 |
40 30 |
40 30 |
Extensibility at break, % - longitudinal direction - transverse direction |
55 - 65 95 - 180 |
55 - 90 130 - 180 |
60 - 95 110 - 140 |
80 - 95 130 - 145 |
The bonding strength of the front coating and the backing, daN/5 cm, not less than - longitudinal direction |
2,5 |
|||
Resistance to dry and wet friction, points, not less than | 4 | |||
Stiffness, cN, not more than group 9-11 group 12 - 17 group 18 - 20 group 21 - 25 |
10 20 40 70 |
|||
Multiple flexing, kilocycles, not less than | 100 | |||
Light resistance, points, for light tones, not less than | 4 | |||
Time of permeability of petroleum products, oils, water, hrs, not less than | 24 |
Fireproof if with a knitted backing
Vinyl artificial upholstery leather is for interiors and seats upholstery, shelf upholstery, etc. for rail and subway trains
Thickness: matched to customer’s wishes
Coating type: PVC100 [%]
Backing type: PES 100 [%]
Flammability: A standard product
Standard width: 145 [cm]
Standard roll sleeve: 40 [m]
Indicator name | Reference | ||
---|---|---|---|
10 | 14 | 20 | |
Breaking load, daN, not less than - longitudinal direction - transverse direction |
20 15 |
30 20 |
40 25 |
Extensibility at break, % - longitudinal direction - transverse direction - diagonal direction |
12 – 30 60 – 110 30 – 60 |
||
Stiffness, cN, not more than | 10 | 20 | 30 |
The bonding strength of the front coating with the backing, daN/5 cm, not less than - longitudinal direction |
3,0 |
||
Wear µg/J, not more than | 84 | ||
Thermal adhesion, kPa, not more than | 98 | ||
Multimple flexing, kilocycles, not less than | 50 | ||
Time of permeability of petroleum products, oils, water, hrs, not less than | 24 |
Skin color can be selected according to the RAL table. The shades may differ due to the unique color rendering of your screen
At the bottom of the table you can see the link wich leads to full range of
RAL colors
Shades of yellow | RAL 1000 | RAL 1001 | RAL 1002 | RAL 1003 | RAL 1004 | RAL 1005 |
Shades of orange | RAL 2000 | RAL 2001 | RAL 2002 | RAL 2003 | RAL 2004 | RAL 2005 |
Shades of red | RAL 3000 | RAL 3001 | RAL 3002 | RAL 3003 | RAL 3004 | RAL 3005 |
Shades of violet | RAL 4000 | RAL 4001 | RAL 4002 | RAL 4003 | RAL 4004 | RAL 4005 |
Shades of blue | RAL 4000 | RAL 4001 | RAL 4002 | RAL 4003 | RAL 4004 | RAL 4005 |
Shades of green | RAL 5000 | RAL 5001 | RAL 5002 | RAL 5003 | RAL 5004 | RAL 5005 |
Shades of grey | RAL 6000 | RAL 6001 | RAL 6002 | RAL 6003 | RAL 6004 | RAL 6005 |
Shades of brown | RAL 7000 | RAL 7001 | RAL 7002 | RAL 7003 | RAL 7004 | RAL 7005 |
Shades of black and white | RAL 8000 | RAL 8001 | RAL 8002 | RAL 8003 | RAL 8004 | RAL 8005 |